| HIPS PH-88S 台湾奇美实业股份有限公司 物性指数 |
| 规格级别： | 挤出级 | 外观颜色： | --- |
| 用途概述： | 押出成型专用 | ||
| 备注说明： | --- | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | --- | ASTM D-1238 | 2.6 | (Cond.G)g/10min |
| 熔体流动速率 | --- | ASTM D-1238 | 8.0 | (Cond.L)g/10min | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.05 | 23/23℃ |
| 机械性能 | 引张强度 | --- | ASTM D-638 | 240(3410) | kg/cm2(lb/in2) |
| 延伸率 | --- | ASTM D-638 | 45 | % | |
| 弯曲弹性率 | --- | ASTM D-790 | 1.8(2.6) | 104kg/cm2(105lb/in2) | |
| 弯曲强度 | --- | ASTM D-790 | 360(5110) | kg/cm2(lb/in2) | |
| 洛式硬度 | --- | ASTM D-785 | 75 | L | |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 12.0(2.20) | kg.cm/cm(ft.lb/in) | |
| IZOD冲击强度 | 1/4" | ASTM D-256 | 10.5(1.93) | kg.cm/cm(ft.lb/in) | |
| 热 性 能 | 维卡软化点 | --- | ASTM D-1525 | 100(212) | ℃(°F) |
| 热变形温度 | --- | ASTM D-648 | 83(181) | ℃(°F) | |
| 燃烧率 | --- | File No E56070 UL&C-CL | 1/16"HB | --- | |