| HIPS PH-88S 镇江奇美有限公司 物性数据 |
| 规格级别： | --- | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | 挤出成型用 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 溶体流动速率 | 200℃,5kg | ASTM D-1238 | 4.5 | g/10min |
| 溶体流动速率 | 200℃,10kg | ISO-1133 | 25 | g/10min | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.05 | --- |
| 机械性能 | 引张强度 | --- | ASTM D-638 | 200 | kg/cm2 |
| 延伸率 | --- | ASTM D-638 | 70 | % | |
| 弯曲弹性率 | --- | ASTM D-790 | 1.7 | 104kg/cm2 | |
| 弯曲强度 | --- | ASTM D-790 | 350 | kg/cm2 | |
| 洛氏硬度 | --- | ASTM D-785 | L-75 | --- | |
| IZOD缺口冲击强度 | 1/8" | ASTM D-256 | 10.5 | Kg-cm/cm | |
| IZOD缺口冲击强度 | 1/4" | ASTM D-256 | 8.0 | Kg-cm/cm | |
| 热 性 能 | 维卡软化点 | --- | ASTM D-1525 | 100 | °C |
| 热变形温度 | --- | ASTM D-648 | 93 | °C | |
| 燃烧率 | --- | UL-94 | HB | --- | |