| MS TX-600S 日本电气化学工业株式会社 物性数据 |
| 暂无此原料描述部分┄ |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔融指数 | 200℃*50N | ASTM D1238 | 1.5 | g/10min |
| 透光率 | 2mm | ASTM D1003 | 92 | % | |
| 阻燃性 | --- | UL 94 | 1.5mmHB | --- | |
| 物理性能 | 雾度 | 2mm | ASTM D1003 | 0.2 | % |
| 比重 | --- | ASTM D792 | 1.12 | --- | |
| 机械性能 | 弯曲强度 | --- | ASTM D790 | 113 | MPa |
| 弯曲弹性模量 | --- | ASTM D790 | 3，390 | MPa | |
| IZOD冲击强度 | 1/4"Notched | ASTM D256 | 20 | J/m | |
| 拉伸强度 | --- | ASTM D638 | 71 | MPa | |
| 成型收缩率 | 2mm | --- | 0.2-0.6 | % | |
| 洛氏硬度 | M scale | ASTM D785 | 89 | --- | |
| 热 性 能 | 维卡软化点 | 50N | ASTM D1525 | 102 | ℃ |
| 热变形温度 | 6.4mm,1.82MPa | ASTM D648 | 87 | ℃ | |