| TPEE 5555HS 美国杜邦公司 物性数据 |
| 暂无此原料描述部分┄ |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||
| 基本性能 | 24小时吸水率 | --- | ASTM D-570 | 0.7 | % | ||||||||
| 物理性能 | 泰伯磨耗量 | CS-17轮 | ASTM D-1044 | - | mg/1000rev | ||||||||
| 比重 | --- | ASTM D-792 | 1.20 | --- | |||||||||
| 熔体流动速率 | --- | ASTM D-1238 | 8.5 | g/10min | |||||||||
| 热畸变温度 | @0.5Mpa | ASTM D-648 | 90 | ℃ | |||||||||
| 泰伯磨耗量 | H 18轮 | ASTM D-1044 | 112 | mg/1000rev | |||||||||
| 机械性能 | 硬度计硬度 | --- | ASTM D-2240 | 55 | --- | ||||||||
| 揉曲模量 | 23℃ | ASTM D-790 | 207 | Mpa | |||||||||
| 断裂拉伸力 | --- | ASTM D-638 | 40 | Mpa | |||||||||
| 断裂伸长 | --- | ASTM D-638 | 500 | % | |||||||||
|
--- |
|
|
|
|||||||||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 不破裂 | J/m | |||||||||
| 初耐撕裂性能 | --- | ASTM D-1004 | 158 | kn/m | |||||||||
| 热 性 能 | 维卡软化点 | --- | ASTM D-1525 | 180 | ℃ | ||||||||
| 熔点 | --- | ASTM D-3418 | 203 | ℃ | |||||||||
| 热畸变温度 | @0.18Mpa | ASTM D-648 | 49 | ℃ | |||||||||
| 其它性能 | 耐揉曲切口增长性能 | --- | ASTM D-1052 | >1×105 | --- | ||||||||