| 牌号 | N225X |
| 厂家(产地) | 沙伯基础(原GE) |
| 密度 | 1.11 g/cm3 |
| 维卡软化点 | 264 ℃ |
聚苯醚PPO N225X沙伯基础(原GE)技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 模塑收缩量flow0.125" | ASTM D-955 | 5-7 | in/in E-3 | |
| 模塑收缩量xflow0.125" | ASTM D-955 | 5-7 | in/in E-3 | |
| 比重固体 | ASTM D-792 | 1.11 | ||
| 仪表控制抗冲击能量 @ 峰值-22F. | ASTM D-3763 | 8.6 | ft-lbs | |
| 拉伸伸长断裂类型 I 0.125" | TM D-638 | 17.0 | % | |
| 伊佐德冲击值反向缺口-22F | ASTM D-256 | 12.0 | ft-lb/in | |
| 抗拉强度屈服类型 I0.125" | ASTM D-638 | 9700 | psi | |
| 伊佐德冲击值缺口73F | ASTM D-256 | 3.5 | ft-lb/in | |
| 挠曲强度屈服0.250 | ASTM D-790 | 14400 | psi | |
| 伊佐德冲击值缺口-22F | ASTM D-256 | 1.8 | ft-lb/in | |
| 挠曲模量0.250" | ASTM D-790 | 361500 | psi | |
| 拉伸伸长屈服类型 I 0.125" | ASTM D-638 | 8.0 | % | |
| 伊佐德冲击值反向缺口73F | ASTM D 256 | 16.6 | ft-lb/in | |
| 仪表控制抗冲击能量 @ 峰值73F. | ASTM D-3763 | 29.0 | ft-lbs | |
| 抗拉强度断裂类型 I0.125" | ASTM D 638 | 7200 | psi | |
| 体积电阻率 | ASTM D-257 | 2 E16 | ohm-cm | |
| 介电常数50 Hz | ASTM D-150 | 2.69 | ||
| 损耗因数1 MHz | ASTM D-150 | 0.0070 | ||
| 介电强度油内125 mils | ASTM D-149 | 414 | V/mil | |
| 介电常数1 MHz | ASTM D-150 | 2.55 | ||
| 损耗因数50 Hz | ASTM D-150 | 0.0100 | ||
| 表面电阻率 | ASTM D-257 | >1 E14 | ohm/sq | |
| UL文件号美国 | E121562 | |||
| V-0 额定值(测试厚度) | UL 94 | 0.060 | inch | |
| HDT(热畸变温度)264 psi0.250" 未退火 | ASTM D-648 | 211 | deg F | |
| 维卡软化温度B级 | ASTM D-1525 | 264 | deg F | |
| 热指数机械冲击性能 | UL 746B | 80 | deg C | |
| 热指数非机械冲击性能 | UL 746B | 95 | deg C | |
| 热指数电性能 | UL 746B | 95 | deg C | |
| 5VA 额定值(测试厚度) | UL 94 | 0.120 | inch | |
| HDT(热畸变温度)66 psi0.250"未退火 | ASTM D-648 | 229 | deg F |