| 牌号 | N127-LD |
| 厂家(产地) | 化学 |
| 硬度 | 82 |
| 弯曲强度 | 98 MPa |
| 拉伸强度 | 61 MPa |
| 弯曲模量 | 2597 MPa |
| 断裂伸长率 | 45 % |
POM N127-LD LG化学技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | ASTM D-570 | 0.22 | % | |
| Taber磨耗量 | ASTM D-1044 | 14 | mg/1000cycles | |
| 比重 | ASTM D-792 | 1.41 | ||
| 模缩系数 | 18～21 | cm/cm×0.0001 | ||
| 伸长率 | TM D-638 | 45 | % | |
| 冲击强度(无缺口) | ASTM D-256 | 70 | kg.cm/cm | |
| 冲击强度(缺口) | ASTM D-256 | 6.0 | kg.cm/cm | |
| 砦挤系数(动) | ASTM D-1894 | 0.16 | ||
| 砦挤系数(静) | ASTM D-1894 | 0.12 | ||
| 张力 | ASTM D-638 | 625 | kg/cm2 | |
| 缩性热伸张系数 | ASTM D-696 | 10×0.000001 | mm/mm/C | |
| 弯曲模量 | ASTM D-790 | 26500 | kg/cm2 | |
| 洛氏硬度 | ASTM D-785 | 82 | M | |
| 弯曲强度 | ASTM D-790 | 1000 | kg/cm2 | |
| 抗表面性 | ASTM D-257 | 1×1016 | Ω | |
| 抗弧性 | ASTM D-495 | 240 | Sec | |
| 介电强度 | ASTM D-149 | 24 | KV/mm | |
| 抗体积性 | ASTM D-257 | 1×1014 | Ω.cm | |
| 介电定数 | ASTM D-150 | 3.8 | ||
| 诱电正接 | ASTM D-150 | 0.007 | ||
| 热变形温度 | 4.6kg/cm2 | ASTM D-648 | 160 | C |
| 燃烧性 | 1/32" | HB | ||
| 热变形温度 | 18kg/cm2 | ASTM D-648 | 110 | C |