| 牌号 | CF-620 |
| 厂家(产地) | LG化学 |
POM CF-620 LG化学技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | ASTM D-570 | 0.35 | % | |
| Taber磨耗量 | ASTM D-1044 | 3 | Taber磨耗量 | |
| 比重 | ASTM D-792 | 1.44 | ||
| 模缩系数 | 4～9.5 | cm/cm×0.0001 | ||
| 洛氏硬度 | ASTM D-785 | 97 | M | |
| 弯曲模数 | ASTM D-790 | 100000 | kg/cm2 | |
| 伸长率 | TM D-638 | 2 | % | |
| 砦挤系数(动) | ASTM D-1894 | 0.13 | ||
| 砦挤系数(静) | ASTM D-1894 | 0.08 | ||
| 张力 | ASTM D-638 | 1200 | kg/cm2 | |
| 弯曲强度 | ASTM D-790 | 1600 | kg/cm2 | |
| 冲击强度(无缺口) | ASTM D-256 | 40 | kg.cm/cm | |
| 冲击强度(缺口) | ASTM D-256 | 5.0 | kg.cm/cm | |
| 带电半减期 | <1 | Sec | ||
| 抗体积性 | ASTM D-257 | <10 | Ω.cm | |
| 抗表面性 | ASTM D-257 | <70 | Ω | |
| 热变形温度 | 4.6kg/cm2 | ASTM D-648 | 166 | C |
| 燃烧性 | HB | |||
| 热变形温度 | 18kg/cm2 | ASTM D-648 | 160 | C |