| 牌号 | HR1000L |
| 厂家(产地) | 日本可乐丽 |
| 规格级别 | 挤出 耐热通用 |
| 密度 | 1.19 g/cm3 |
| 熔体流动速率 | 2.1 g/10min |
| 成型收缩率 | 0.004 % |
| 缺口冲击强度 | 1.6 |
| 吸水率 | 0.3 % |
PMMA HR1000L日本可乐丽物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | ASTM D-570 | 0.3 | % | |
| 熔体流动速率 | 230℃/3.8kgs | ASTM D-1238 | 2.1 | g/10min |
| 收缩率 | ASTM D-955 | 0.002-0.006 | % | |
| 总透光率 | ASTM D-1003 | 93 | % | |
| 折射率 | ASTM D-542 | 1.49 | ||
| 比重 | ASTM D-792 | 1.19 | ||
| 弯曲弹性率 | ASTM D-790 | 35000 | kg/cm2 | |
| 拉伸强度 | ASTM D-638 | 7 | % | |
| 抗拉强度 | ASTM D-638 | 770 | kg/cm2 | |
| IZOD缺口冲击强度 | ASTM D-256 | 1.6 | kg.cm/cm | |
| 洛氏硬度 | ASTM D-785 | 105 | M scale | |
| 抗挠强度 | ASTM D-790 | 1240 | kg/cm2 | |
| 热变形温度 | 有退火 | ASTM D-648 | 106 | ℃ |
| 燃烧性 | UL 94 | HB | CLASS | |
| 维卡软化点 | ASTM D-1525 | 118 | ℃ | |
| 热变形温度 | 无退火 | ASTM D-648 | 97 | ℃ |
| 贝兹 | ASTM D-1003 | 0.3 | % |