| 牌号 | IR-H70 |
| 厂家(产地) | 三菱丽阳 |
| 密度 | 1.14 g/cm3 |
| 熔体流动速率 | 0.7 g/10min |
| 拉伸强度 | 32 MPa |
| 成型收缩率 | 0.6 % |
| 吸水率 | 0.4 % |
PMMA IR-H70三菱丽阳物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | 24hr | ASTM D-570 | 0.4 | % |
| 熔体流动速率 | 230°C.3.8kg | ASTM D-1238 | 0.7 | g/10min |
| 成形收缩率 | ASTM D-955 | 0.4-0.8 | % | |
| 全光线透射系数 | 3.2mm | ASTM D-1003 | 92 | % |
| 比重 | ASTM D-792 | 1.14 | ||
| 折射率 | nd | ASTM D-542 | 1.49 | |
| 洛氏硬度 | M scale | ASTM D-785 | 37 | |
| 延展率 | ASTM NO.1 | ASTM D-638 | 90 | % |
| 抗拉强度 | ASTM NO.1 | ASTM D-638 | 330 | Kg/cm2 |
| 抗弯强度 | 1/4"棒 | ASTM D-790 | 460 | Kg/cm2 |
| 悬臂梁式冲击强度 | 1/4" | ASTM D-256 | 7 | kg.cm/cm |
| 弯曲弹性模量 | 1/4"棒 | ASTM D-790 | 1.3×104 | Kg/cm2 |
| 介质损耗角正切 | JIS K-6911 | 0.04 | ||
| 介质损耗角正切 | 60HZ | JIS K-6911 | 0.04 | |
| 体积电阻系数 | JIS K-6911 | >1×1015 | Ω.m | |
| 耐电弧性 | JIS K-6911 | 没有痕迹 | ||
| 绝缘击穿强度 | JIS K-6911 | 15 | kv/mm | |
| 介电常数 | 60HZ | JIS K-6911 | 3.9 | |
| 面电阻系数 | JIS K-6911 | >1×1016 | ||
| 线膨胀系数 | ASTM D-696 | 11.5×10-5 | cm/cm/°C | |
| 维卡软化点 | 1kg | ASTM D-1525 | 105 | °C |
| 载荷挠曲温度 | 18.56kg/cm2 | ASTM D-648 | 90 | °C |
| 比热 | 0.35 | cal/g/°C | ||
| 热传导系数 | ASTM C-177 | 5×10-4 | cal/s/cm/°C |