| 牌号 | IF860 |
| 厂家(产地) | LG化学 |
| 规格级别 | 注塑 |
| 密度 | 1.18 g/cm3 |
| 熔体流动速率 | 16 g/10min |
| 弯曲强度 | 128 MPa |
| 弯曲模量 | 3295 MPa |
| 吸水率 | 0.3 % |
PMMA IF860 LG化学物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 比重 | ASTM D792 | 1.18 | g/cm3 | |
| 吸水率 | 24hr | ASTM D570 | 0.3 | % |
| 流动指数 | 230℃,3.8kg | ASTM D1238 | 16 | g/10min |
| 洛氏硬度 | M-scale | ASTM D785 | 94 | |
| IZOD冲击强度 | with notch | ASTM D256 | 1.5 | kgcm/cm2 |
| 拉力 | ASTM D638 | 660 | Kg/cm2 | |
| 延伸率 | ASTM D638 | 10 | Kg/cm2 | |
| 弯曲强度 | ASTM D790 | 1.310 | Kg/cm2 | |
| 弯曲模量 | ASTM D790 | 33600 | Kg/cm2 | |
| 维卡软化点 | 1kg | ASTM D1525 | 104 | C |
| 热变形温度 | 未退火,18.5kg/cm2 | ASTM D648 | 84 | C |
| 线性膨胀系数 | ASTM D696 | 6*10-5 | cm/cm/C | |
| 折射率 | nd | ASTM D542 | 1.49 | |
| 透明性 | 3mm | ASTM D1003 | 92 | % |
| 黄色度 | 3mm | ASTM D1925 | 0.4 | % |
| HAZE | 3mm | ASTM D1003 | 0.5 | % |