| 牌号 | GF-320 |
| 厂家(产地) | 台湾健日佳 |
| 规格级别 | 增强 纤维 |
| 密度 | 1.5 g/cm3 |
| 熔体流动速率 | 0 g/10min |
| 成型收缩率 | 0.2 % |
| 缺口冲击强度 | 0 |
| 吸水率 | 0.07 % |
增强PET GF-320台湾健日佳物性数据
| 性能 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| (密度,) | ASTM D792 | 1.5 | g/cm3 | |
| (吸水性,) | 50%,23℃,24h | ASTM D570 | 0.07 | % |
| (成型收缩率,) | ASTM D955 | 0.2-0.4 | % | |
| (拉伸强度,) | 10mm/min | ASTM D638 | 107 | MPa |
| (断裂伸长率,) | 10mm/min | ASTM D638 | 2.6 | % |
| (弯曲强度,) | 2mm/min | ASTM D790 | 158 | MPa |
| (弯曲模量,) | 2mm/min | ASTM D790 | 5860 | MPa |
| (Izod缺口冲击强度,) | 23℃ | ASTM D256 | 110 | J/M |
| (面电阻率,) | ASTM D257 | 1E13 | ||
| (体积电阻率,) | ASTM D257 | 1E15 | .cm | |
| (热变形温度,) | 0.46MPa | ASTM D648 | 244 | ℃ |
| (热变形温度,) | 1.82MPa | ASTM D648 | 215 | ℃ |
| (硬度,) | ScaleR | ASTM D785 | 120 | |
| (熔点,) | ASTM D3418 | 254 | ℃ |