| 牌号 | IN2200S |
| 厂家(产地) | 日本出光 |
| 规格级别 | 注塑级 |
| 用途 | 眼药容器、角腊接触镜片盒、人造肾 |
注塑级PC IN2200S日本出光技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 熔体流动速率 | 300℃ | ISO 1133 | 12 | g/10min |
| 吸水率 | 23℃，24时间 | ASTM D-570 | 0.23 | % |
| 光线透过率 | 3mm | ASTM D-1003 | 85～89 | % |
| 比重 | ASTM D-792 | 1.20 | ||
| 拉伸强度 | ASTM D-638 | 68 | MPa | |
| 塔泊磨损 | ASTM D-1044 | 12 | Mg | |
| 挠曲强度 | TM D-790 | 93 | MPa | |
| 弯曲模量 | ASTM D-790 | 2350 | MPa | |
| IZOD缺口冲击强度 | ASTM D-256 | 70 | KJ/m2 | |
| 洛氏硬度 | ASTM D-785 | R-120 | ||
| 拉伸模量 | ASTM D-638 | 2300 | MPa | |
| 断裂伸长率 | ASTM D-638 | 115 | % | |
| 拉伸强度 | ASTM D-638 | 64 | MPa | |
| 绝缘破坏电压 | 1.6mm | ASTM D-149 | 30 | Kv/mm |
| 抗电弧 | ASTM D-495 | 110 | SEc | |
| 介电常数 | 60HZ | ASTM D-150 | 2.91 | |
| 介电耗损正接 | 60HZ | ASTM D-150 | 6.6×10-4 | |
| 体积固有抵抗 | ASTM D-257 | 1016< | Ω.cm | |
| 成型收缩率 | ASTM D-955 | 0.5-0.7 | % | |
| 负荷挠曲温度 | 1.8MPa | ASTM D-648 | 132 | ℃ |
| 阻燃性 | 1.47mm | UL 94 | V-2 | |
| 线膨胀系数 | ASTM D-696 | 6.5 | ×10-5 | |
| 维卡软化温度 | ISO 306 | 148 | ℃ |