| 牌号 | FR50 |
| 厂家(产地) | 美国杜邦 |
| 规格级别 | 注塑 |
| 密度 | 1.56 g/cm3 |
| 拉伸强度 | 169 MPa |
| 断裂伸长率 | 2.5 % |
| 缺口冲击强度 | 100 |
| 吸水率 | 0.5 % |
PA66/FR50/美国杜邦技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | 24hr | ASTM D-570 | DAM｜50%RH,0.5｜- | % |
| 比重 | ASTM D-792 | DAM｜50%RH,1.56｜- | ||
| 模具收缩率 | 3.2mm flow | ASTM D-792 | DAM｜50%RH,0.4｜- | % |
| 弯曲强度 | ASTM D-790 | DAM｜50%RH,240｜- | MPa | |
| 断裂伸长率 | TM D-638 | DAM｜50%RH,2.5｜4 | % | |
| IZOD缺口冲击强度 | ASTM D-256 | DAM｜50%RH,100｜105 | J/m | |
| 弯曲模量 | ASTM D-790 | DAM｜50%RH,8960｜6900 | MPa | |
| 拉伸强度 | ASTM D-638 | DAM｜50%RH,169｜134 | MPa | |
| 体积电阻率 | ASTM D-257 | DAM｜50%RH,10,14,｜10,11 | Ω.cm | |
| 损耗因数 | 103Hz | ASTM D-150 | DAM｜50%RH,DAM｜50%RH,0.｜541,0.009｜0.113 | |
| 介电常数 | 103Hz | ASTM D-150 | DAM｜50%RH,3.6｜5.1 | |
| 表面电阻率 | ASTM D-257 | DAM｜50%RH,10,14,｜10,11 | Ω | |
| 介电强度 | 3.2mm | ASTM D-149 | DAM｜50%RH,17.2｜15.6 | kv/mm |
| 损耗因数 | 106Hz | ASTM D-150 | DAM｜50%RH,0.014｜0.041 | |
| 介电常数 | 106Hz | ASTM D-150 | DAM｜50%RH,3.5｜3.8 | |
| 热变形温度 | 0.45MPa | ASMT D-648 | DAM｜50%RH,257｜- | ℃ |
| 热变形温度 | 1.80MPa | ASTM D-648 | DAM｜50%RH,235｜- | MPa |
| 熔点 | ASTM D-3418 | DAM｜50%RH,262｜- | ℃ |