| 牌号 | GF43 LE BK |
| 厂家(产地) | 美国TPC |
| 规格级别 | 热稳定 |
| 密度 | 1.5 g/cm3 |
| 熔体流动速率 | 4 g/10min |
| 成型收缩率 | 0.3 % |
| 缺口冲击强度 | 123 |
| 吸水率 | 1 % |
PA6/GF43 LE BK/美国TPC技术数据
| 性能 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 比重 | ASTM D-792 | 1.5 | g/cm3 | |
| 熔体流动速率 | 230℃/2.16kg | ASTM D-1238 | 4 | g/10min |
| 吸水率 | 24hr | ASTM D-570 | 1 | % |
| 成型收缩率-Flow | 3.18mm | ASTM D-955 | 0.3 | % |
| 洛氏硬度 | R-Scale | ASTM D-785 | 121 | |
| 拉伸屈服强度 | ASTM D-638 | 200 | MPa | |
| 拉伸断裂伸长率 | ASTM D-638 | 2 | % | |
| 弯曲模量 | ASTM D-790 | 10300 | MPa | |
| 弯曲强度 | ASTM D-790 | 248 | MPa | |
| 悬臂梁缺口冲击强度 | 3.18mm | ASTM D-256 | 123 | J/m |
| 悬臂梁缺口冲击强度 | 3.18mm | ASTM D-256 | 1120 | J/m |
| 热变形温度 | 1.8MPa, Unannea | ASTM D-648 | 210 | ℃ |
| 热变形温度 | 0.45MPa, Unannealed | ASTM D-648 | 216 | ℃ |
| 线膨胀系数-Flow | ASTM D-696 | 0.000016 | cm/cm/℃ | |
| 体积电阻率 | ASTM D-257 | 1.0E+15 | ohmcm | |
| 介电强度 | ASTM D-149 | 18 | kV/mm |