| 牌号 | CM1011G-30 |
| 厂家(产地) | 日本东丽 |
| 规格级别 | 注塑 |
| 密度 | 1.36 g/cm3 |
| 弯曲强度 | 254.9 MPa |
| 断裂伸长率 | 5 % |
| 缺口冲击强度 | 11 |
| 吸水率 | 1.1 % |
PA6/CM1011G-30/日本东丽技术数据
| 性能 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | 23℃，24小时 | 无水｜2.5%水,,1.1｜-, | % | |
| 比重 | ASTM D-792 | 无水｜2.5%水,,1.36｜-, | ||
| IZOD冲击强度 | 无缺口1/8，23℃ | 无水｜2.5%水,,80｜100, | kgcm/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 无水｜2.5%水,,1500｜1000, | Kg/cm2 |
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜2.5%水,,890｜700, | Kg/cm2 |
| 断裂伸长率 | 80℃ | ASTM D-638 | 无水｜2.5%水,,6｜-, | % |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜2.5%水,,5｜5, | % |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜2.5%水,,120｜-, | R-标度 |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜2.5%水,,93｜-, | M-标度 |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 无水｜2.5%水,,1000｜700, | Kg/cm2 |
| 挠曲模量 | -40℃ | ASTM D-790 | 无水｜2.5%水,,108000｜90000, | Kg/cm2 |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜2.5%水,,2600｜1400, | Kg/cm2 |
| 压缩强度 | -40℃ | ASTM D-695 | 无水｜2.5%水,,2500｜-, | Kg/cm2 |
| 压缩强度 | 80℃ | ASTM D-695 | 无水｜2.5%水,,970｜-, | Kg/cm2 |
| 挠曲模量 | 80℃ | ASTM D-790 | 无水｜2.5%水,,43000｜34000, | Kg/cm2 |
| 断裂伸长率 | -40℃ | ASTM D-638 | 无水｜2.5%水,,4.5｜-, | % |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜2.5%水,,80000｜48000, | Kg/cm2 |
| 挠曲强度 | -40℃ | ASTM D-790 | 无水｜2.5%水,,3100｜3000, | Kg/cm2 |
| 抗剪强度 | 80℃ | ASTM D-792 | 无水｜2.5%水,,7000｜520, | Kg/cm2 |
| 压缩强度 | 23℃ | ASTM D-695 | 无水｜2.5%水,,1800｜-, | Kg/cm2 |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 无水｜2.5%水,,2550｜2300, | Kg/cm2 |
| IZOD冲击强度 | V-缺口1/2，-40℃ | ASTM D-256 | 无水｜2.5%水,,8.5｜14, | kgcm/cm2 |
| 泰伯磨耗量 | (1000g CS-17)23℃ | ASTM D-1044 | 无水｜2.5%水,,12｜-, | mg/1000次 |
| IZOD冲击强度 | 无缺口1/8，-40℃ | 无水｜2.5%水,,68｜79, | kgcm/cm2 | |
| IZOD冲击强度 | V-缺口1/2，23℃ | ASTM D-256 | 无水｜2.5%水,,11｜19, | kgcm/cm2 |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜2.5%水,,1700｜1050, | Kg/cm2 |
| 抗电弧性 | 1/8" | ASTM D-495 | 无水｜2.5%水,,131｜137, | 秒 |
| 介电常数 | 50Hz | ASTM D-150 | 无水｜2.5%水,,4.9｜10.7, | |
| 体积电阻率 | ASTM D-257 | 无水｜2.5%水,,10,15,｜10,12, | .cm | |
| 损耗因数 | 50Hz | ASTM D-150 | 无水｜2.5%水,,0.03｜0.17, | |
| 损耗因数 | 103Hz | ASTM D-150 | 无水｜2.5%水,,0.03｜0.18, | |
| 介电常数 | 103Hz | ASTM D-150 | 无水｜2.5%水,,4.6｜7.9, | |
| 损耗因数 | 106Hz | ASTM D-150 | 无水｜2.5%水,,0.02｜0.07, | |
| 介电强度 | 1/8" | ASTM D-149 | 无水｜2.5%水,,20｜18, | KV/mm |
| 介电常数 | 106Hz | ASTM D-150 | 无水｜2.5%水,,4.0｜4.3, | |
| 导热系数 | 无水｜2.5%水,,0.23｜-, | Kcal/mhr℃ | ||
| 熔点 | 差示扫描测热计DSC | 无水｜2.5%水,,225｜-, | ℃ | |
| 线性热膨胀系数 | ASTM D-696 | 无水｜2.5%水,,2-3｜-, | 10-5cm/cm/℃ | |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 无水｜2.5%水,,224｜-, | ℃ |
| UL-94抗燃级 | UL 94 | 无水｜2.5%水,,无水｜2.5%水,,UL-94｜-,,HB(1/16")｜-, | ||
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 无水｜2.5%水,,215｜-, | ℃ |
| 比热 | 无水｜2.5%水,,0.32｜-, | Cal/g℃ | ||
| 强化含量 | 无水｜2.5%水,,30｜-, | WT% |