| 牌号 | B102F |
| 厂家(产地) | 南京立汉 |
PA6/B102F/南京立汉技术数据
| 性能 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 饱合吸水率 | ASTM D-570 | 9.5 | % | |
| 密度 | 干态 | ASTM D-792 | 1.13 | g/cm3 |
| 模塑收缩率 | 纵向 | ASTM D-955 | 1.0-1.4 | mm/mm/100 |
| 悬臂梁缺口冲击强度 | 干态 | ASTM D-256 | 45 | J/M |
| 断裂伸长率 | 湿态 | ASTM D-638 | >50 | % |
| 弯曲模量 | 湿态 | ASTM D-790 | 850 | MPa |
| 弯曲强度 | 湿态 | ASTM D-790 | 50 | MPa |
| 悬臂梁缺口冲击强度 | 湿态 | ASTM D-256 | 160 | J/M |
| 断裂伸长率 | 干态 | ASTM D-638 | >50 | % |
| 洛氏硬度 | 干态 | ASTM D-785 | 119 | R |
| 弯曲模量 | 干态 | ASTM D-790 | 2450 | MPa |
| 拉伸强度 | 湿态 | ASTM D-638 | 50 | MPa |
| 弯曲强度 | 干态 | ASTM D-790 | 110 | MPa |
| 拉伸强度 | 干态 | ASTM D-638 | 80 | MPa |
| 介电强度一瞬间 | 湿度 | ASTM D-149 | 29 | KV/mm |
| 面电阻率 | 湿态 | ASTM D-257 | 1.00×1010 | Ω |
| 介电强度一瞬间 | 干态 | ASTM D-149 | 35 | KV/mm |
| 表面电阻率 | 干态 | ASTM D-257 | 1.00×1013 | Ω |
| 燃烧性 | UL94 | V2 | ||
| 熔点 | DSC | ASTM D-3417 | 220 | °C |
| 热变形温度 | 1.8MPa | ASTM D-648 | 55-75 | °C |
| 热变形温度 | 0.45MPa | ASTM D-648 | 182 | °C |