| 牌号 | CM1017 |
| 厂家(产地) | 日本东丽 |
| 规格级别 | 注塑 |
| 密度 | 1.13 g/cm3 |
| 弯曲强度 | 107.84 MPa |
| 弯曲模量 | 2843.14 MPa |
| 断裂伸长率 | 180 % |
| 吸水率 | 1.8 % |
PA6/CM1017/日本东丽技术数据
| 性能 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜3.5%水,1.8｜- | % |
| 泰伯磨耗量 | 1000g CS-17 | ASTM D-1044 | 无水｜3.5%水,3-4｜- | mg/1000次 |
| 比重 | ASTM D-792 | 无水｜3.5%水,1.12-1.14｜- | ||
| IZOD冲击强度 | 无缺口1/2"，23℃ | 无水｜3.5%水,5｜40 | kg.cm/cm | |
| IZOD冲击强度 | -40℃，无缺口1/2 | 无水｜3.5%水,3.5｜15 | kg.cm/cm | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜3.5%水,180｜ | % |
| 搞剪强度 | 23℃ | ASTM D-732 | 无水｜3.5%水,740｜690 | Kg/cm2 |
| 挠曲强度 | 80℃ | ASTM D-790 | 无水｜3.5%水,500｜300 | Kg/cm2 |
| 挠曲强度 | -40℃ | ASTM D-790 | 无水｜3.5%水,1500｜1450 | Kg/cm2 |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜3.5%水,119｜90 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜3.5%水,820｜420 | Kg/cm2 |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 无水｜3.5%水,320｜220 | Kg/cm2 |
| 抗拉屈服强度 | -40 | ASTM D-638 | 无水｜3.5%水,1230｜1150 | Kg/cm2 |
| 挠曲模量 | -40℃ | ASTM D-790 | 无水｜3.5%水,40000｜37000 | Kg/cm2 |
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 无水｜3.5%水,20｜- | Kg/cm2 |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜3.5%水,29000｜10000 | Kg/cm2 |
| 压缩强度 | 23℃ | ASTM D-695 | 无水｜3.5%水,890｜- | Kg/cm2 |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜3.5%水,83｜- | |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜3.5%水,1100｜450 | Kg/cm2 |
| 挠曲模量 | 80℃ | ASTM D-790 | 无水｜3.5%水,8000｜4000 | Kg/cm2 |
| IZOD冲击强度 | 23℃，无缺口1/8 | 无水｜3.5%水,无断裂｜- | kg.cm/cm | |
| 体积电阻率 | ASTM D-257 | 无水｜3.5%水,10,14,-10,15,｜10,11,-10,12 | Ω.cm | |
| 损耗因素 | 106Hz | ASTM D-150 | 无水｜3.5%水,0.03｜- | |
| 介电强度 | 1/8" | ASTM D-149 | 无水｜3.5%水,20｜- | KV/mm |
| 损耗因素 | 50Hz | ASTM D-150 | 无水｜3.5%水,无水｜3.5%水,0.07｜-,50Hz｜- | |
| IEC导电径踪指数 | UL 746 | 无水｜3.5%水,≤600｜- | V | |
| 介电常数 | 106Hz | ASTM D-150 | 无水｜3.5%水,3.9｜- | |
| 损耗因素 | 103Hz | ASTM D-150 | 无水｜3.5%水,0.06｜- | |
| 抗电弧性 | 1/8" | ASTM D-150 | 无水｜3.5%水,121｜- | |
| 介电常数 | 50HZ | ASTM D-150 | 无水｜3.5%水,4.1｜- | |
| 介电常数 | 106Hz | ASTM D-150 | 无水｜3.5%水,3.4｜- | |
| 导热系数 | 无水｜3.5%水,0.18｜- | Kcal/m.hr.°C | ||
| 线性热膨胀系数 | ASTM D-696 | 无水｜3.5%水,8｜- | 10-5cm/cm.℃ | |
| 比热 | 无水｜3.5%水,0.46｜- | Cal/g.°C | ||
| 热挠曲温度 | ASTM D-648 | 无水｜3.5%水,190｜- | ℃ | |
| 熔点 | 差示扫描测热计DSC法 | 无水｜3.5%水,225｜- | ℃ | |
| UL-94抗燃级 | UL 94 | 无水｜3.5%水,V-2(1/16")｜- | ||
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 无水｜3.5%水,190｜- | ℃ |