| 牌号 | NB100 |
| 厂家(产地) | 南京利华 |
| 规格级别 | 注塑级 |
| 用途 | 用于挤出尼龙管，尼龙板等 |
PA6/NB100/南京利华技术数据
| 性能 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 熔体流动速率 | ASTM D-1238 | 0.4-1.4 | g/10min | |
| 吸水率 | 24hr | ASTM D-570 | 0.9 | % |
| 密度 | ASTM D-792 | 1.20 | g/cm3 | |
| 吸水率 | 饱和 | ASTM D-570 | 4.0 | % |
| 线性成型收缩率 | ASTM D-955 | 0.01-0.015 | mm/mm | |
| 拉伸强度 | 断裂 | ASTM D-638 | 80 | Mpa |
| 弯曲模量 | ASTM D-790 | 2950 | Mpa | |
| 悬臂梁缺口冲击强度 | ASTM D-256 | 3.5 | KJ/m2 | |
| 断裂伸长率 | ASTM D-638 | 25 | % | |
| 弯曲强度 | 屈服 | ASTM D-790 | 115 | Mpa |
| 洛氏硬度 | R120 | |||
| 介电强度 | ASTM D-149 | 17 | KV/mm | |
| 面电阻 | ASTM D-257 | 1013 | ohm | |
| 注射成型时的参考模温 | 60-80 | ℃ | ||
| 烘干温度/时间 | 90/4-6 | ℃/hr | ||
| 注塑成型温度范围 | 230-265 | ℃ | ||
| 热变形温度 | 0.45MPa/1.81MPa | ASTM D-648 | 200/90 | ℃ |
| 阻燃等级 | UL 94 | HB |