| 牌号 | CL |
| 厂家(产地) | 美国T |
| 规格级别 | 透明 |
| 用途 | 清除，透明 |
| 密度 | 1.06 g/cm3 |
| 熔体流动速率 | 12 g/10min |
| 成型收缩率 | 1.1 % |
| 缺口冲击强度 | 53.4 |
| 吸水率 | 0.3 % |
PA12/CL/美国TPC技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 比重 | ASTM D-792 | 1.06 | g/cm3 | |
| 熔体流动速率 | 230℃/3.8kg | ASTM D-1238 | 12 | g/10min |
| 吸水率 | 24hr | ASTM D-570 | 0.3 | % |
| 成型收缩率-Flow | 3.18mm | TM D-955 | 1.1 | % |
| 洛氏硬度 | M-Scale | ASTM D-785 | 85 | |
| 拉伸屈服强度 | ASTM D-638 | 81.4 | MPa | |
| 拉伸屈服伸长率 | ASTM D-638 | 10 | % | |
| 弯曲模量 | ASTM D-790 | 2030 | MPa | |
| 弯曲强度 | ASTM D-790 | 98.6 | MPa | |
| 悬臂梁缺口冲击强度 | 3.18mm | ASTM D-256 | 53.4 | J/m |
| 热变形温度 | 0.45MPa，Unannealed | ASTM D-648 | 154 | ℃ |
| 热变形温度 | 1.8MPa，Unannea | ASTM D-648 | 149 | ℃ |
| 维卡软化点 | ASTM D-1525 | 108 | ℃ | |
| 线膨胀系数-Flow | ASTM D-696 | 0.000072 | cm/cm/℃ | |
| 透射 | ASTM D-1003 | 89-90 | % | |
| 雾度 | ASTM D-1003 | 0.7 | % |