| LDPE 1816H 扬子石化巴斯夫有限责任公司 物性数据 |
| 规格级别： | 注塑级 | 外观颜色： | --- |
| 用途概述： | 内衬 | ||
| 备注说明： | --- | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||
| 基本性能 | 熔体流动速率 | 190℃/2.16kg | --- | 1.3-1.8 | g/10min | ||||||||
| 密度 | --- | --- | 0.917-0.921 | g/cm3 | |||||||||
| 机械性能 | 屈服拉伸强度 | --- | ISO 527 | >8 | N/mm2 | ||||||||
| 弹性模量（拉伸） | --- | ISO 527 | >180 | N/mm2 | |||||||||
| 光泽度 | 20℃ | ASTM D-2457 | >12 | --- | |||||||||
|
--- |
|
|
|
|||||||||
|
--- |
|
|
|
|||||||||
| 热 性 能 | 熔融温度 | --- | ISO 306 | >104 | ℃ | ||||||||
| 维卡软化温度 | --- | ISO 306 | >84 | ℃ | |||||||||
| 其它性能 | 薄膜厚度 | --- | --- | 50 | µm | ||||||||
| 浊度 | --- | ASTM D-1003 | <14 | % | |||||||||
| 落镖 | --- | ASTM D-1709 | >100 | g | |||||||||
| 增滑剂 | --- | --- | 400-600 | ppm | |||||||||
| 开口剂 | --- | --- | 1650-1950 | ppm | |||||||||