| 牌号 | UE629 |
| 厂家(产地) | 台湾聚合 |
| 规格级别 | 发泡级 |
| 用途 | 鞋底发泡 |
| 密度 | 0.939 g/cm3 |
| 硬度 | 31 |
| 熔体流动速率 | 2.5 g/10min |
| 缺口冲击强度 | 430 |
| 维卡软化点 | 64 ℃ |
鞋底发泡EVA UE629台湾聚合物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 射出 | ASTM D-638/D-882 | 220 | % | |
| 铸膜成型 | ASTM D-638/D-882 | 750 | % | |
| 薄膜(MD) | ASTM D-638/D-882 | 250 | kg/cm2 | |
| 薄膜(TD) | ASTM D-638/D-882 | 240 | kg/cm2 | |
| 薄膜(MD) | ASTM D-638/D-882 | 480 | % | |
| 薄膜(TD) | TM D-638/D-882 | 640 | % | |
| 冲击强度 | ASTM D-1709 | 430 | G/F50 | |
| 射出 | ASTM D-638/D-882 | 117 | kg/cm2 | |
| VA含量 | ASTM USIFE | 18 | % | |
| 密度 | ASTM D-1505 | 0.939 | g/cm3 | |
| 融化点 | ASTM D-2117 | 86 | ℃ | |
| VICAT 软化点 | ASTM D-1525 | 64 | ℃ | |
| 熔融指数 | ASTM D-1238 | 2.5 | g/10min | |
| 低温易脆性 | ASTM D-746 | <-76 | ℃/F50 | |
| 硬度 | ASTM D-2240 | 31 | Shore D | |
| 铸膜成型 | ASTM D-638/D-882 | 180 | kg/cm2 |