| 牌号 | UE508 |
| 厂家(产地) | 台湾塑胶 |
| 规格级别 | 热熔级 |
| 用途 | 粉末热融(用于不织布热融胶) |
| 密度 | 0.925 g/cm3 |
| 硬度 | 36 |
| 熔体流动速率 | 75 g/10min |
| 拉伸强度 | 7 MPa |
| 断裂伸长率 | 400 % |
热熔级EVA台湾塑胶物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 密度 | ASTM D-1505 | 0.925 | g/cm3 | |
| 熔体流动速率 | ASTM D-1238 | 75 | g/10min | |
| 硬度 | ASTM D-2240 | 36 | Shore D | |
| 延展性(铸膜成型) | ASTM D-638(ASTM D-882) | 400 | % | |
| 延展性(射出) | ASTM D-638(ASTM D-882) | - | % | |
| 延展性(薄膜MD) | TM D-638(ASTM D-882) | - | % | |
| 延展性(薄膜TD) | ASTM D-638(ASTM D-882) | - | % | |
| 低温易脆性 | ASTM D-746 | ＜-76 | ℃/F50 | |
| 降伏点抗张强度(铸膜成型) | ASTM D-638(ASTM D-882) | 80 | KG/cm2 | |
| 降伏点抗张强度(射出) | ASTM D-638(ASTM D-882) | - | KG/cm2 | |
| 降伏点抗张强度(薄膜MD) | ASTM D-638(ASTM D-882) | - | KG/cm2 | |
| 降伏点抗张强度(薄膜TD) | ASTM D-638(ASTM D-882) | - | KG/cm2 | |
| 维卡软化点 | ASTM D-1525 | 70 | ℃ | |
| 熔点 | ASTM D-2117 | 96 | ℃ | |
| VA含量 | USIFE | 8 | % |