| 牌号 | LD 768.MJ Blown |
| 厂家(产地) | 埃克森美孚 |
EVA LD 768.MJ Blown埃克森美孚物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 熔流率 | 190C/2.16 kg | ASTM D1238 | 2.3 | g/10 min |
| 醋酸乙烯含量 | ExxonMobil Method | 26.2 | wt% | |
| 割线模量 | 1% 正割, MD | ASTM D882 | 29.2 | MPa |
| 1% 正割, TD | ASTM D882 | 31.4 | MPa | |
| 抗张强度 | MD: 断裂 | TM D882 | 35.1 | MPa |
| TD: 断裂 | ASTM D882 | 34.7 | MPa | |
| 伸长率 | MD: 断裂 | ASTM D882 | 450 | % |
| TD: 断裂 | ASTM D882 | 730 | % | |
| 落锤冲击 | ASTM D1709A | 460 | g | |
| 埃尔曼多夫抗撕强度 | MD | ASTM D1922 | 38 | g |
| TD | ASTM D1922 | 460 | g | |
| 维卡软化温度 | ASTM D1525 | 48.0 | C |